| 论文题目 | A comparative investigation on the corrosion degradation of plasma sprayed YSZ and LnMgAl11O19 (Ln=Nd, Sm, Gd) coatings exposed to the molten V2O5+Na2SO4 salt mixture at 1100 ℃ |
| 作 者 | ; Xiaolong Chen*,Yiwei Sun, Dexin Chen, Jie Li, Wei Li, Dahai Zeng, Duoli Wu, Xueqiang Cao |
| 发表年度 | OCT 2019 |
| 刊物名称 | JOURNAL OF THE EUROPEAN CERAMIC SOCIETY |
| 卷、期、页码 | 39; 13; 3778-3787 |
| 影响因子 | |
| 论文摘要 | Corrosive attack of the molten 50 wt. % V2O5 + 50 wt.% Na2SO4 salt mixture has been comparably studied for the APS YSZ and LnMgAl(11)O(19) (LnMA, Ln = Nd, Sm, Gd) thermal barrier coatings upon a 10 h anneal at 1100 degrees C in air. The YSZ coating suffered from a deepest infiltration of the molten salt along its thickness direction through the open and connected pores as well as inter-lamellae microcracks. A large number of newly formed voids were widely distributed in the YSZ coating due to the corrosion degradation followed by the t, t' to m-ZrO2 phase transformation. While, a relative thin corrosion layer mainly consisting of alpha-Al2O3 and LnVO(4) were present for the corroded LnMA coatings. The much reduced number of open pores and connected microcracks together with the rapid chemical reaction between the molten salt and LnMA coatings, especially for the NdMA coating, preventing further infiltration of the molten salt, was beneficial to mitigate further attacks to the inner coating at the expense of sacrificing a thinner top layer. The presences of amorphous phases were thought to further accelerate the corrosion reaction and strengthen such a corrosion protection mode for all the APS LnMA coatings. |
| 全文链接 | https://www.sciencedirect.com/science/article/pii/S0955221919303036?via%3Dihub |
| 附件地址 |
研究队伍